dc.description.abstractLos aceros inoxidables son un grupo de aceros de alta aleación que poseen una buena resistencia a la corrosión en diferentes ambientes. Esta característica se debe al contenido de cromo que tienen en su composición (superior al 10%), el cual forma una película delgada de óxido que lo aísla del ambiente agresivo, por lo cual estos aceros son muy utilizados en la industria alimenticia, petroquímica, médica, etc. Estos aceros de acuerdo a su estructura se pueden clasificar en ferríticos, austeníticos y martensíticos. Estos últimos poseen buenas propiedades mecánicas y aceptable resistencia a la corrosión. Para mejorar sus propiedades superficiales, pueden ser sometidos a tratamientosde modificación superficial asistidos por plasma. La nitruración iónica es una buenaopción para incrementar la dureza superficial y resistencia al desgaste en estos aceros,sin disminuir la resistencia a la corrosión característica del material. En este trabajo se realizaron diferentes ensayos de nitruración, analizando comoafecta a la capa modificada la variación del tiempo y la temperatura de los mismos, sobre un único sustrato de acero inoxidable martensítico, el AISI 420. De acuerdo a los resultados obtenidos, puede indicarse que con tratamientos de corta duración y mayor temperatura se obtienen valores similares de dureza y espesor de capa que en los tratamientos tradicionales. En cuanto al comportamiento a la corrosión y al desgaste, algunos de los tratamientos cortos de nitruración presentaron una mayor resistencia en ambas propiedades que los ensayos característicos de largo tiempo.es_ES
dc.description.abstractStainless steels are a group of high alloy steels that have good resistance corrosion in different environments. This characteristic is due to their chromium content (greater than 10%), which allow forming an oxide film that isolates it from the aggressive environment, so these steels are used in the food, petrochemical, and medical industry. These steels can be subjected to plasma-assisted surface modification treatments in order to improve their surface properties. Plasma nitriding is a good technique to increase the surface hardness and wear resistance without affecting the corrosion resistance of the material. In this work, nitriding was carried out in different conditions, the influence of the variation of process time and temperature on the nitrided layer formation for AISI 420 martensitic stainless steel was studied. According to the results, it can be indicated that with treatments of short time and higher temperature, similar hardness and layer thickness values to the of traditional treatments can be obtained. With respect to the corrosion and wear resistance, some of the short nitriding treatments showed better behavior than the long treatments.es_ES
dc.formatapplication/pdfes_ES
dc.language.isospaes_ES
dc.publisherUniversidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay.es_ES
dc.rightsinfo:eu-repo/semantics/openAccesses_ES
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/4.0/*
dc.rights.uriAttribution-NonCommercial-NoDerivatives 4.0 Internacional*
dc.subjectAcero inoxidablees_ES
dc.subjectNitruraciónes_ES
dc.subjectDesgastees_ES
dc.subjectCorrosiónes_ES
dc.titleEstudio de las condiciones óptimas de nitruración iónica para el acero AISI 420es_ES
dc.typeinfo:eu-repo/semantics/bachelorThesises_ES
dc.rights.holderRegis, Matías Sebastiánes_ES
dc.description.affiliationFil: Regis, Matías Sebastián. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay; Argentina.es_ES
dc.type.versioninfo:eu-repo/semantics/acceptedVersiones_ES
dc.type.snrdinfo:ar-repo/semantics/tesis de gradoes_ES
dc.rights.useNo comercial con fines académicos.es_ES


Files in this item

Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record

info:eu-repo/semantics/openAccess
Except where otherwise noted, this item's license is described as info:eu-repo/semantics/openAccess