Browsing by Author "Gomez, Martín"
Now showing 1 - 3 of 3
- Results Per Page
- Sort Options
Item Comportamiento magnético del acero AISI 304 en ensayos de tracción uniaxial(2018-07-19) Neyra Astudillo, Miriam Rocio; Scagnetti, Hugo Juan; Nuñez, Nicolás; Ferrari, Guido; López Pumarega, Isabel; Gomez, Martín; Ruzzante, José; Padovese Rodrigues, LinilsonDurante el proceso de magnetización de un material ferromagnético, las paredes de los dominios magnéticos son forzadas a moverse bajo la influencia del campo magnético. Para que las paredes se puedan mover deben superar la resistencia producida por los puntos de anclaje (borde de grano, dislocaciones, inclusiones, etc.), ocasionando saltos discretos en la magnetización. Estos saltos se pueden detectar con una bobina sensora colocada sobre la superficie de la muestra, que los transforma en pulsos de voltaje. Estos últimos son conocidos como Ruido Magnético Barkhausen (RMB). En este trabajo se continúa el estudio de ensayos de tracción uniaxial, hasta rotura, en probetas de acero AISI 304 (no magnético), en las cuales, como consecuencia de la deformación, aparece una fase ferromagnética que sí produce RMB. Las mediciones se realizaron a diferentes cargas con el fin de observar cómo cambiaban las características del RMB. A partir de las señales obtenidas en las mediciones, se diseñó un filtro digital con el propósito de eliminar todo tipo de señal espuria e individualizar el RMB. Para tal propósito se utilizó un filtro digital Butterworth con banda pasante (2- 200) kHz. La selección del tipo de filtro se debe a que éste presenta una respuesta prácticamente constante hasta la frecuencia de corte, obteniéndose una respuesta plana a lo largo de la banda pasante. Para cada valor de carga se analizaron por separado las señales de RMB respecto de las etapas de aumento y disminución del campo magnético de excitación. Con el objetivo de caracterizar cada etapa, se estimaron diversos parámetros estadísticos que fueron evaluados en función de la deformación aplicada. Por último se calculó la evolución temporal de las señales y su función cuadrática media (RMS) para cada etapa de la magnetización, realizándose la correlación cruzada con el propósito de evaluar el grado de semejanza existente entre cada parte de la señal.Item Evaluation of plastic deformation in steels with magnetic and acoustic techniques(2020-02-06) Neyra Astudillo, Miriam Rocio; Nuñez, Nicolás; López Pumarega, Isabel; Ruzzante, José; Gomez, MartínBarkhausen Magnetic Noise (MBN) and Magnetic Acoustic Emission (MAE) are phenomena that occur in ferromagnetic materials which undergo changes in their magnetization. These phenomena are very sensitive to changes on microstructure and residual stresses. The MBN and MAE can be applied as monitoring techniques to detect plastic deformation in materials subjected to thermomechanical processes, such as machining and manufacturing processes. In this work, the plastic deformation in samples subjected to uniaxial tensile tests is investigated through MBN and MAE. Twelve stainless steel test pieces of two different materials (AISI 430 and AISI 441A), were tested. As a first step, in order to obtain their mechanical properties, two test pieces of each material cut in different directions with respect to the rolling direction, were tested up to rupture. The others were deformed in four stages on plastic deformation. After each stage, MBN and MAE measurements were made, in order to obtain a correlation with the strain and the magnetic situation of the materials. We present here the microstructural analyses, the study of MBN and MAE signals, correlating them with the state of deformation of the specimens.Item Ruido Magnético Barkhausen y Emisión Magneto Acústica en probetas de aleación Fe-1 wt % Cu(2009-11) Gomez, Martín; López Pumarega, Isabel; Torres, Darío; Nuñez, Nicolás; Armeite, María; Ruzzante, JoséTanto el Ruido Barkhausen (RB) como la Emisión Magneto Acústica (EMA), en materiales ferromagnéticos, dependen de las características microestructurales de los mismos y forman parte de las técnicas de caracterización no destructivas. El aumento de la vida útil de los reactores nucleares en servicio es de interés mundial, siendo la integridad de los recipientes de presión un aspecto fundamental a resolver. Estos recipientes de presión están construidos en aceros ferríticos de baja aleación con presencia crítica de impurezas tales como el Cu. Por otro lado, son bien conocidos los efectos perjudiciales de la presencia de Cu en aleaciones base Fe debido a que su segregación en borde de grano fragiliza su microestructura. En este trabajo se utilizaron probetas de Fe-1wt % Cu realizadas en Japón y que son parte de un “Segundo Ensayo Inter-Laboratorios”. Para simular la degradación y el proceso de envejecimiento producido en aceros de recipientes de presión de reactores nucleares, sin necesidad de irradiación, se realizaron sobre las probetas distintos tratamientos tanto térmicos como mecánicos. Cabe destacar que las muestras fueron tratadas en el país de origen. En este trabajo se presentan los primeros resultados de las mediciones de RB, EMA, rugosidad y conductividad. Se comparan el RMS (Root Mean Square) de las diversas señales y se las asocia con los cambios microestructurales que surgen de los distintos tratamientos termomecánicos.