Analysis of DTA and dilatometric data used to study the behaviour of a mould flux
(2019-06-01)
In the present work a casting powder containing ≈ 36 wt% SiO2, ≈ 31 wt% CaO, 13 wt% Na2O, and 10 wt% CaF2, was used as starting material. A mass of 10 g of the mould powder was placed in a graphite crucible and melted at ...
Replacement of fluorine in mould powders: influence on the crystallization kinetics
(Springer, 2019-06-01)
In the present work mould powders were prepared using different raw materials. One powder was fluorine-containing and the others were free-F. The total fluorine content (approx. 10 wt%) was replaced by different percentages ...
Thermal analysis techniques applied to study wear mechanisms of black refractories used in the steel continuous casting process
(Springer, 2019-06-01)
In this paper, the results are correlated with information obtained through conventional techniques such as optical microscopy (OM) and scanning electron microscopy (SEM) including EDS analysis and EBSD, that are used to ...
Viscosidad de polvos coladores: comparación entre valores experimentales y modelos teóricos
(Universidad Nacional de Rosario, 2019-10-01)
En este trabajo se presenta el desarrollo, montaje y puesta en servicio de un equipo para realizar mediciones de viscosidad a altas temperaturas. En particular, se mide la viscosidad de tres polvos coladores comerciales ...
Correlación entre viscosidad y estructuras vítreas obtenidas a partir de polvos coladores fundidos
(Universidad Nacional de Rosario, 2019-10-01)
En el presente trabajo se analiza, por medio de difracción de rayos X (DRX) y espectroscopia Raman, la
estructura de tres polvos coladores comerciales, obtenidos por enfriamiento rápido (templado) desde la
fusión (1300°C). ...
Failure caused by multiple mechanisms that produce a premature localized wear of a steel ladle slag line
(Research Waves Ltd., 2020-08-30)
A post mortem MgO-C brick of a steel ladle (slag line) was studied to identify the main causes of a localized wear, produced at initial taps. The extreme low thickness of the lining provokes ladle removed from service. In ...
Formación de fases en compuestos de matriz metálica base hierro reforzada con carburos
(Centro Científico Tecnológico CONICET Mar del Plata, 2022-05-06)
En el presente trabajo, se diseñaron dos compuestos de matriz metálica reforzada con partículas (CMMRP), denominados A y B, de bajo punto de fusión mediante modelado termodinámico con el software FactSage, teniendo en ...
Medición de viscosidad de escorias a altas temperaturas y su impacto sobre la eficiencia de los procesos pirometalúrgicos
(Universidad Nacional de San Juan. Facultad de Ingeniería, 2021-09-17)
El presente trabajo presenta resultados de mediciones de viscosidad de escorias utilizadas en el proceso de colada continua de aceros de ultra bajo contenido de carbono (ULC) en el rango de 1200°C a 1350°C, empleando un ...
Análisis comparativo de dos compuestos de matriz metálica reforzada aplicados como recubrimientos duros
(Universidad Tecnológica Nacional, 2022-11-04)
Las aleaciones de matriz metálica base Fe se utilizan ampliamente en la ingeniería de superficies para proporcionar resistencia al desgaste de componentes cuyas superficies están sujetas a condiciones tribológicas severas. ...
Parámetros asociados a la viscosidad de materiales vítreos: caso de escorias siderúrgicas
(Universidad Nacional de La Plata, 2022-11-18)
En el presente trabajo se analiza la relación de la longitud de las capas obtenidas en los ensayos de plano inclinado con la viscosidad teórica (T), estimada a partir de la composición química de las distintas escorias. ...