Browsing by Author "Trava-Airoldi, Vladimir Jesús"
Now showing 1 - 16 of 16
- Results Per Page
- Sort Options
Item Carbon based coatings deposited on stainless steel : study of thermal degradation(2017-03-02) Dalibón Bähler, Eugenia Laura; Trava-Airoldi, Vladimir Jesús; Brühl, Sonia Patricia; Ghafoor, Naureen; Rogström, Lina; Odén, MagnusAmorphous hydrogenated carbon (DLC) coatings have a high hardness depending on the relative amount of sp3/sp2 bondings. They also exhibit an extremaly low friction coefficient and are chemically inert. However, these coatings have some disadvantages which limit their applications. For instance, adhesion is poor when are deposited on metallic substrates and they are also unstable at high temperatures, degrading into graphite and loosing hardness. in this work, DLC coatings were deposited on presipitation hardening stainless steel (PH Corrax) which was plasma nitrided before the coating deposition. The samples were submitted to annealing treatments for an hour at different temperatures from 200 to 600ºC, together with a control group, wich was only coated but not nitrided. After each annealing cycle, Raman Spectroscopy, nanoindentation and microscopy were used to check fil properties. It was demonstrated that the nitriding pretreatment improved not only adhesion but also the thermal stability of the DLC, slowing degradation and preventing delamination.Item Characterization of DLC coatings over nitrided stainless steel with and without nitriding pre-treatment using annealing cycles(2019-04-02) Dalibón Bähler, Eugenia Laura; Czerwiec, Thierry; Trava-Airoldi, Vladimir Jesús; Ghafoor, Naureen; Rogström, Lina; Odén, Magnus; Brühl, Sonia PatriciaAmorphous hydrogenated diamond-like carbon (DLC) coatings were deposited using plasma assisted chemical vapour deposition (PACVD) on precipitation hardening (PH) stainless steel. Plasma nitriding has been used as pre-treatment to enhance adhesion and mechanical properties. Chemical and mechanical properties of DLC coatings are dependent on the hydrogen content and so on the relation between sp3 /sp2 bondings. The bondings and the structure of the DLC film change with temperature. In this work, a study of the thermal degradation and the evolution of the mechanical properties of DLC coatings over PH stainless steel have been carried out, including the effect of an additional nitrided layer. Nitrided and non-nitrided steel samples were subjected to the same coated in the same conditions, and they were submitted to the same thermal cycles, heating from room temperature to 600 C in several steps. After each cycle, Raman spectra and surface topography measurements were performed ◦ and analyzed. Nanohardness measurements and tribological tests, using a pin-on-disc machine, were carried out to analyze variations in the friction coefficient and the wear resistance. The duplex sample, with nitriding as pre-treatment showed a better thermal stability. For duplex sample, the coating properties, such as adhesion, and friction coefficient were sustained after annealing at higher temperatures; whereas it was not the case for only coated sample.Item Comportamiento mecánico de un recubrimiento DLC depositado sobre acero inoxidable martensítico previamente nitrurado(2013-05-07) Dalibón Bähler, Eugenia Laura; Charadía, Raúl; Cabo, Amado; Trava-Airoldi, Vladimir Jesús; Brühl, Sonia PatriciaEn este trabajo se estudió el comportamiento tribológico de un film de DLC que fue depositado sobre acero inoxidable martensítico AISI 420 nitrurado, con dos terminaciones superficiales diferentes, previas a la nitruración iónica, analizando los resultados en función del acabado superficial.Item Comportamiento mecánico de un recubrimiento DLC sobre acero AISI 420 nitrurado por plasma con diferentes terminaciones superficiales(2013-02-25) Brühl, Sonia Patricia; Charadía, Raúl; Dalibón Bähler, Eugenia Laura; Trava-Airoldi, Vladimir Jesús; Cabo, AmadoEn este trabajo se estudió el comportamiento tribológico de un film de DLC depositado sobre acero inoxidable martensítico.Item Corrosion resistance of DLC hard coatings deposited over nitrided PH stainless steel(2014-07-23) Cabo, Amado; Trava-Airoldi, Vladimir Jesús; Dalibón Bähler, Eugenia Laura; Brühl, Sonia Patricia; Pereira, Lânia AuxiliadoraIn this work a DLC film was deposited over ion nitrided PH stainless steel Corrax® with a Si interlayer in a CVD Plasma, where the plasma was generated and sustained by an asymmetric pulsed DC discharge. A nitrided sample was compared in all tests with a DLC coated sample and a duplex one (nitrided+coating). Nitriding has been carried out in an industrial facility with a pulsed DC discharge.Item DLC multilayers to improve fretting and corrosion resistance over nitrided martensitic stainless steel(2018-09-20) Brühl, Sonia Patricia; Dalibón Bähler, Eugenia Laura; Trava-Airoldi, Vladimir JesúsIn this work, the fretting wear and corrosion behavior of DLC multilayers coatings were studied and compared to the monolayer coating.Item Estudio del comportamiento mecánico de recubrimientos DLC multicapa depositados sobre el acero inoxidable martensítico nitrurado(2019-10-02) Dalibón Bähler, Eugenia Laura; Brühl, Sonia Patricia; Cabo, Amado; Pecina, Jorge Nahuel; Trava-Airoldi, Vladimir Jesús; Caballero, Mario AlbertoEl acero inoxidable martensítico AISI 420 posee diferentes aplicaciones en la industria donde se requiere buena resistencia al desgaste y a la corrosión. Para mejorar sus propiedades superficiales, algunos tratamientos pueden ser aplicados como recubrimientos “Diamond Like Carbon” (DLC) que se caracterizan por su buena resistencia al desgaste, bajo coeficiente de fricción y ser químicamente inertes. Sin embargo presentan problemas de adhesión cuando son depositados sobre sustratos metálicos entonces un pretratamiento como la nitruración asistida por plasma puede resultar conveniente.Item Fretting wear resistance of DLC hard coatings deposited on nitrided martensitic stainless steel(2019-03) Dalibón Bähler, Eugenia Laura; Pecina, Jorge Nahuel; Cabo, Amado; Trava-Airoldi, Vladimir Jesús; Brühl, Sonia PatriciaIn this work, the fretting wear behavior and adhesion of DLC coatings deposited by PACVD on nitrided and non-nitrided martensitic stainless steels were studied. Fretting wear tests were carried out with different duration and loads and pin-on-disk was also performed. The adhesion was evaluated by Rockwell C indentation and scratch test with constant and variable loads. The coating thickness was 2.5 m and the nitrided layer, 11 m. The coating hardness and Young’s Modulus were about 16 and 110 GPa, respectively. The duplex samples resulted with better adhesion than the only coated samples in all test conditions. In the scratch test, the critical load in the duplex sample was 58 N and in the coated sample, 12 N, showing a brittle failure mode. In the Rockwell C indentation test, the adhesion was better in the duplex sample because the nitriding treatment changed the failure mode of the system. The wear resistance was also related to adhesion, since in the experiments with high loads and long durations adhesive failures could be detected when stresses reached the interfac and the substrate. In the duplex sample, the nitrided case, with higher load bearing capacit than the substrate, resulted in a better wear behavior of the system.Item Influence of the silicon interlayer deposition process in the adhesion of the DLC coatings deposited on nitrided martensitic stainless steel(2017-08-25) Dalibón Bähler, Eugenia Laura; Lugo González, Dubrazkha Carolina; Ramírez Ramos, Marco Antonio; Trava-Airoldi, Vladimir Jesús; Brühl, Sonia PatriciaThe DLC coatings are characterized by good wear resistance, low friction coefficient and chemical inertness [1]. However, they have adhesion problems when they are deposited on metallic substrates. For this reason, a thin interlayer of different materials, such as silicon, is deposited previous to the coating in order to improve the adhesion. There are a few studies about the influence of the conditions of the silicon interlayer deposition on adhesion or properties of the coatings [2,3]. In this work, the adhesion of DLC coatings deposited on nitrided and non-nitrided martensitic stainless steel, modifying the silicon interlayer bias potential deposition, is studied.Item Influence of the silicon interlayer deposition process in the adhesion of the DLC coatings deposited on nitrided martesnitic stainless steel(2017-08-25) Dalibón Bähler, Eugenia Laura; Brühl, Sonia Patricia; Trava-Airoldi, Vladimir Jesús; Ramírez Ramos, Marco Antonio; Lugo González, Dubrazkha CarolinaThe DLC coatings are characterized by good wear resistance, low friction coefficient and chemical inertness. However, they have adhesion problems when they are deposited on metallic substrates. For thisreason, a thin interlayer of different materials, such as silicon, is deposited previous to the coating in order to improve the adhesion. There are a few studies about the influence of the conditions of the silicon interlayer deposition on adhesion or properties of the coatings [2,3]. In this work, the adhesion of DLC coatings deposited on nitrided and non-nitrided martensitic stainless steel, modifying the silicon interlayer bias potential deposition, is studied.Item Mechanical and corrosion behaviour of DLC and TiN coatings deposited on martensitic stainless steel(2017-09-10) Dalibón Bähler, Eugenia Laura; Pecina, Jorge Nahuel; Moscatelli, Mauro Nicolás; Ramírez, Marco Antonio; Trava-Airoldi, Vladimir Jesús; Brühl, Sonia PatriciaThe objective of this work is to compare the wear, friction, adhesion and corrosion behaviour of commercial TiN and DLC coatings deposited on AISI 420 stainless steel.Item Mechanical properties and corrosion behaviour of DLC monolayers and multilayers deposited over nitrided martensitic stainless steel(2019-09-24) Brühl, Sonia Patricia; Dalibón Bähler, Eugenia Laura; Cabo, Amado; Trava-Airoldi, Vladimir JesúsDLC coatings have unique properties such as very low coefficient of criction and chemical inertness and they are used extensively as protection and solid lubricants in many industrial applications. Nevertheless, adhesion over certain substrates like stainless steel has many unresolved issues, as well as corrosion mechanisms are not well understood.Item Protección de acero para instrumentos quirúrgicos con recubrimientos duros en base carbono tipo DLC(2018-07-19) Pecina, Jorge Nahuel; Brühl, Sonia Patricia; Cabo, Amado; Trava-Airoldi, Vladimir Jesús; Dalibón Bähler, Eugenia LauraLos aceros inoxidables martensíticos como el AISI 420 tienen múltiples aplicaciones, entre ellas instrumentos quirúrgicos, donde se requiere buena resistencia al desgaste y a la corrosión. Los tratamientos de modificación superficial, como la nitruración iónica, permiten mejorar las propiedades mecánicas de estos aceros pero afectan su resistencia a la corrosión. Por esta razón, un tratamiento posterior de deposición de recubrimiento tipo DLC (“Diamond Like Carbon”, carbono símil diamante) puede ser conveniente. En este trabaj se estudió el comportamiento al desgaste y a la corrosión de muestras dúplex (nitruradas y recubiertas por PACVD) y se compararon con muestras nitruradas, sólo recubiertas, nitruradas y sólo templadas y revenidas. Se analizaron los recubrimientos con espectroscopia Raman y EDS. Se realizaron ensayos de desgaste tipo “pin on disk” y se evaluó la adhesión mediante ensayos de Scratch Test e indentación Rockwell C. Se midió nanodureza con indentador Berkovich. Se llevaron a cabo los ensayos propuestos para instrumentos quirúrgicos en la Norma F 1089-02 (prueba de agua hirviendo y de hisopado con sulfato de cobre) y ensayos de niebla salina. Estos recubrimientos tienen una relación ID/I de 0,8 y bajo contenido de hidrógeno aproximadamente del 20 %. El espesor de los recubrimientos fue de 2 µm y la dureza alcanzó 24 GPa. La capa nitrurada tuvo un espesor de 10 µm. Las muestras dúplex y recubierta presentaron bajo coeficiente de fricción y el volumen desgastado fue indetectable. Además, tuvieron buen comportamiento a la corrosión en el ensayo de niebla salina y en los ensayos propuestos en la Norma ASTM F 1089-02. No obstante, la muestra sólo nitrurada presentó una región corroída en el ensayo de sulfato de cobre y en el de agua hirviendo. La muestra dúplex presentó mejor adhesión que la muestra sólo recubierta en los ensayos de Scratch Test y de indentación Rockwell C.Item Protección de acero para instrumentos quirúrgicos con recubrimientos duros en base carbono tipo DLC(2016-11-22) Dalibón Bähler, Eugenia Laura; Pecina, Jorge Nahuel; Brühl, Sonia Patricia; Cabo, Amado; Trava-Airoldi, Vladimir JesúsLos aceros inoxidables martensíticos como el AISI 420 tienen múltiples aplicaciones, entre ellas instrumentos quirúrgicos, donde se requiere buena resistencia al desgaste y a la corrosión. Los tratamientos de modificación superficial, como la nitruración iónica, permiten mejorar las propiedades mecánicas de estos aceros pero afectan su resistencia a la corrosión. Por esta razón, un tratamiento posterior de deposición de un recubrimiento tipo DLC (Diamond Like Carbon) puede ser conveniente. En este trabajo se estudió el comportamiento al desgaste y a la corrosión de muestras dúplex (nitruradas y recubiertas por PACVD) y se compararon con muestras nitruradas, sólo recubiertas, nitruradas y sin ningún tratamiento más que templado y revenido. Se analizaron los recubrimientos con espectroscopia Raman y EDS. Se realizaron ensayos de pin on disk y se evaluó la adhesión mediante ensayos de Scratch Test e indentación Rockwell C. Se midió nanodureza con indentador Berkovich. Se llevaron a cabo los ensayos propuestos para instrumentos quirúrgicos en la Norma F 1089-02 (prueba de agua hirviendo y de hisopado con sulfato de cobre) y ensayos de corrosión en niebla salina. Estos recubrimientos tienen bajo contenido de hidrógeno, aproximadamente un 20 %. El espesor de los recubrimientos fue de 2 μm y la dureza alcanzó 24 GPa. La capa nitrurada tuvo un espesor de 10 μm. Las muestras dúplex y recubiertas presentaron bajo coeficiente de fricción y el volumen desgastado fue indetectable. Además, tuvieron buen comportamiento a la corrosión en el ensayo de niebla salina y en los ensayos propuestos en la Norma F 1089-02. No obstante, la muestra sólo nitrurada presentó una región corroída en el ensayo de sulfato de cobre y en el de agua hirviendo. La muestra dúplex presentó mejor adhesión que la muestra sólo recubierta en los ensayos de Scratch Test y de indentación Rockwell C.Item Thermal stability of DLC coating deposited on precipitation hardening stainless steels(2015-11-17) Dalibón Bähler, Eugenia Laura; Ghafoor, Naureen; Rogström, Lina; Trava-Airoldi, Vladimir Jesús; Odén, Magnus; Brühl, Sonia PatriciaRelationship between nanohardness and annealing temperature of DLC coating on duplex (previously nitrided) and only coated PH steel samples.Item Wear resistance of nitrided and DLC coated PH stainless steel(2013-05-27) Dalibón Bähler, Eugenia Laura; Brühl, Sonia Patricia; Trava-Airoldi, Vladimir JesúsIn this work PH stainless steel Corrax(R) was ion nitrided and coated with DLC in a CVD process.