Incidence of heat treatment on the corrosive behavior of AISI 316L austenitic stainless steel
(2023-06-30)Heat treatments of AISI 316L samples were conducted at 900°C with slow cooling in air to induce varied precipitation of chromiumrich carbide particles at grain boundaries, resulting in a microstructure susceptible to ... -
Incidencia del hidrógeno atrapado sobre el comportamiento mecánico de acero inoxidable AISI 316L tratado térmicamente
(2021-06-25)En este estudio se presentan los resultados de la investigación para evaluar las posibles interacciones entre un ambiente hidrogenado altamente agresivo y las tensiones uniaxiales aplicadas mediante ensayos mecánicos de ... -
Influence of electroplating stages on hydrogen pickup in SAE 1005 steel.
(2018-05-10)Hydrogen embrittlement is a common, dangerous, but poorly understood cause of failure in metals and alloys. In coated samples, coatings act as a barrier to hydrogen damage resulting in a decrease in the corrosion rate and ... -
Influencia del hidrógeno gaseoso sobre las propiedades mecánicas de un acero de alta resistencia
(2018-10-24)La Fragilización Inducida por Hidrógeno (FIH) se ha investigado a través de los años mediante la aplicación de técnicas de carga electrolíticasde H, más rápidas y sencillas de llevar a cabo. Sin embargo, éstas no pueden ... -
Medición de viscosidad de escorias a altas temperaturas y su impacto sobre la eficiencia de los procesos pirometalúrgicos
(Universidad Nacional de San Juan. Facultad de Ingeniería, 2021-09-17)El presente trabajo presenta resultados de mediciones de viscosidad de escorias utilizadas en el proceso de colada continua de aceros de ultra bajo contenido de carbono (ULC) en el rango de 1200°C a 1350°C, empleando un ... -
Mejora en las propiedades mecánicas a alta temperatura de ladrillos refractarios
(Universidad Tecnológica Nacional, 2021-09-20)El propósito de este trabajo es comparar el comportamiento mecánico, en compresión, de tres ladrillos de MgO-C, conformados a partir de dos diferentes calidades de magnesia. El contenido de MgO, material carbonoso y otros, ... -
Parámetros asociados a la viscosidad de materiales vítreos: caso de escorias siderúrgicas
(Universidad Nacional de La Plata, 2022-11-18)En el presente trabajo se analiza la relación de la longitud de las capas obtenidas en los ensayos de plano inclinado con la viscosidad teórica (T), estimada a partir de la composición química de las distintas escorias. ... -
Relación entre propiedades térmicas y mecánicas con la viscosidad de escorias usadas en el colado de aceros
(Universidad de la República Uruguay, 2023-04-21)En el presente trabajo se determina la fluidez de diversas escorias de molde, con y sin flúor, a la temperatura de 1300ºC, por medio del método del plano inclinado. Las capas sólidas obtenidas tras el enfriamiento rápido ... -
Replacement of fluorine in mould powders: influence on the crystallization kinetics
(Springer, 2019-06-01)In the present work mould powders were prepared using different raw materials. One powder was fluorine-containing and the others were free-F. The total fluorine content (approx. 10 wt%) was replaced by different percentages ... -
Salt spray test on AISI 316L stainless steel
(2020-01-10)Damage produced by rigorous working conditions can affect materials, especially when they are exposed to high temperatures, corrosive atmospheres and mechanical stresses. Austenitic stainless steels have variable chromium ... -
Sensitización microestructural en acero inoxidable austenítico AISI 316L
(2022-11-08)A pesar de los numerosos intentos por desarrollar aceros inoxidables austeníticos con adiciones intencionales de elementos de aleación para mitigar las reacciones corrosivas que pueden originarse durante el servicio en ... -
Structural evolution of a Al2O3-MgOxAl2O3 castable in the range 1000-1600ºC
(The American Ceramic Society, 2022-07-28)Thermal and structural characteristics of an alumina-spinel castable (containing 2.5 wt.% CaO) was studied. The specimens were cast (8.0 wt.% water), cured in air at ambient temperature (48 h), then dried at 100°C (24 h) ... -
Structural evolution of an Al2O3-MgO•Al2O3 castable in the range 1000-1600°C
(Mind Authors Inc., 2020-11-10)Thermal and structural characteristics of an alumina-spinel castable (containing 2.5 wt.% CaO) was studied. The specimens were cast (8.0 wt.% water), cured in air at ambient temperature (48 h), then dried at 100°C (24 h) ... -
Structure-viscosity relationship in mold fluxes using spectroscopy techniques
In this work, glassy layers of three commercial mold fluxes were obtained by quenching from 1300°C. These layers were characterized by XRD, Raman and XPS spectroscopy. The viscosity of these materials, measured between ... -
Thermal analysis techniques applied to study wear mechanisms of black refractories used in the steel continuous casting process
(Springer, 2019-06-01)In this paper, the results are correlated with information obtained through conventional techniques such as optical microscopy (OM) and scanning electron microscopy (SEM) including EDS analysis and EBSD, that are used to ... -
Tratamientos térmicos y corrosión en niebla salina en acero inoxidable AISI 316L
(Universidad Tecnológica Nacional, 2020-10-06)En este trabajo se evalúa el comportamiento microestructural de un acero inoxidable AISI 316L, tratado térmicamente y sometido a ensayos de corrosión acelerada, durante 96 horas, en cámara de niebla salina según normas ... -
Viscosidad de polvos coladores: comparación entre valores experimentales y modelos teóricos
(Universidad Nacional de Rosario, 2019-10-01)En este trabajo se presenta el desarrollo, montaje y puesta en servicio de un equipo para realizar mediciones de viscosidad a altas temperaturas. En particular, se mide la viscosidad de tres polvos coladores comerciales ...