Parámetros asociados a la viscosidad de materiales vítreos: caso de escorias siderúrgicas
(Universidad Nacional de La Plata, 2022-11-18)En el presente trabajo se analiza la relación de la longitud de las capas obtenidas en los ensayos de plano inclinado con la viscosidad teórica (T), estimada a partir de la composición química de las distintas escorias. ... -
Relación entre propiedades térmicas y mecánicas con la viscosidad de escorias usadas en el colado de aceros
(Universidad de la República Uruguay, 2023-04-21)En el presente trabajo se determina la fluidez de diversas escorias de molde, con y sin flúor, a la temperatura de 1300ºC, por medio del método del plano inclinado. Las capas sólidas obtenidas tras el enfriamiento rápido ... -
Replacement of fluorine in mould powders: influence on the crystallization kinetics
(Springer, 2019-06-01)In the present work mould powders were prepared using different raw materials. One powder was fluorine-containing and the others were free-F. The total fluorine content (approx. 10 wt%) was replaced by different percentages ... -
Structural evolution of a Al2O3-MgOxAl2O3 castable in the range 1000-1600ºC
(The American Ceramic Society, 2022-07-28)Thermal and structural characteristics of an alumina-spinel castable (containing 2.5 wt.% CaO) was studied. The specimens were cast (8.0 wt.% water), cured in air at ambient temperature (48 h), then dried at 100°C (24 h) ... -
Structural evolution of an Al2O3-MgO•Al2O3 castable in the range 1000-1600°C
(Mind Authors Inc., 2020-11-10)Thermal and structural characteristics of an alumina-spinel castable (containing 2.5 wt.% CaO) was studied. The specimens were cast (8.0 wt.% water), cured in air at ambient temperature (48 h), then dried at 100°C (24 h) ... -
Structure-viscosity relationship in mold fluxes using spectroscopy techniques
In this work, glassy layers of three commercial mold fluxes were obtained by quenching from 1300°C. These layers were characterized by XRD, Raman and XPS spectroscopy. The viscosity of these materials, measured between ... -
Thermal analysis techniques applied to study wear mechanisms of black refractories used in the steel continuous casting process
(Springer, 2019-06-01)In this paper, the results are correlated with information obtained through conventional techniques such as optical microscopy (OM) and scanning electron microscopy (SEM) including EDS analysis and EBSD, that are used to ... -
Viscosidad de polvos coladores: comparación entre valores experimentales y modelos teóricos
(Universidad Nacional de Rosario, 2019-10-01)En este trabajo se presenta el desarrollo, montaje y puesta en servicio de un equipo para realizar mediciones de viscosidad a altas temperaturas. En particular, se mide la viscosidad de tres polvos coladores comerciales ...