    Análisis de las propiedades de ladrillos cerámicos alivianados obtenidos a partir de arcilla y agregados de diversos residuos agroindustriales.
    (AACINI. Revista Internacional de Ingeniería Industrial, 2024-11-24) Pelozo, Gisela; Quaranta, Nancy Esther; Caligaris, Marta Graciela
    Numerosas investigaciones fueron realizadas incorporando diversos residuos agroindustriales a mezclas arcillosas, con el fin de producir materiales cerámicos alivianados. En este trabajo se han analizado algunos de estos estudios, tomando como partida aquellos que se desarrollaron en las mismas condiciones experimentales, de tal forma que las variables a analizar son las densidades de las biomasas, y el porcentaje de residuo adicionado. Los descartes biomásicos seleccionados son cáscaras de maní, cáscaras de pistacho, carozos de aceitunas, marlos de maíz, entre otros. La caracterización de estos materiales se realizó con diversas técnicas. Los diagramas de XRD presentan en todos los casos los picos característicos de la porción cristalina de la celulosa. Por su parte los estudios de comportamiento térmico muestran picos exotérmicos correspondientes a los procesos de combustión-descomposición de los biopolímeros presentes. Se han estudiado las propiedades y características de los productos cerámicos obtenidos, pudiéndose observar que, en todos los casos, para contenidos de hasta 10% de material residual, se cumplen los requerimientos del mercado para este tipo de ladrillos. Además, un análisis detallado de la forma y tamaño de los poros producidos en las muestras ha conducido a establecer una importante relación con las características de las partículas de biomasas agregadas.
  • Thumbnail Image
    Item
    Ceramic bricks using pistachio shells as controlled porosity former
    (University Amar Telidji - Laghouat, 2023-03-27) Quaranta, Nancy Esther; Caligaris, Marta Graciela; Unsen, Miguel Angel; López, Hugo Arbelio; Pelozo, Gisela Guadalupe; Cristóbal, Adrián Alberto
    The present work studies the use of pistachio shells as a porosity-forming raw material in the manufacture of ceramic bricks. It focuses on the characteristics of the ceramic pieces obtained with different residual biomass contents (from 5 to 20% by volume). The specimens were shaped by uniaxial pressure of 25 MPa, and then were treated at 950°C for 3h. Based on the results obtained it is possible to conclude that the use of this residual biomass, as a pore former in the ceramic industry is feasible. The proportion of added biomass that generates the best characteristics and properties in the final product is 10%. Up to this percentage of aggregate, ceramic pieces with very good macroscopic and microscopic characteristics are obtained, with porosity and flexural strength values that meet market requirements for this type of product. Optical microscopy technique has been used to carry out a detailed analysis of the shape and size of the formed pores, which is a specific objective of this work. It has been observed that for contents of 5 and 10% biomass, the shape of pores is similar to the shape of the particles of added pistachio shells, while for higher contents (15 and 20%) it is different with elongated characteristics. In relation with the size of the pores, at lower contents is around 60% of the original particles size, and for the higher percentages of biomass, they are larger, indicating that agglomerates of particles are formed and when combusted, produce that porosity characteristics.
  • Thumbnail Image
    Item
    Uso de marlo de maíz como generador de porosidad controlada en cerámicos
    (Universidad Tecnológica Nacional, 2023-02-22) Quaranta, Nancy Esther; Varoli, Romina Soledad; Caligaris, Marta Graciela; Cristóbal, Adrián Alberto
    El objetivo de este trabajo es analizar la utilización de marlos de maíz, como material formador de poros en la fabricación de materiales cerámicos alivianados. Las materias primas, marlo molido y arcilla, fueron exhaustivamente caracterizadas. Los productos cerámicos estudiados se fabricaron a partir de arcilla comercial con el agregado de 5%, 10% y 15% en volumen de marlos, y una muestra sin biomasa adicionada a modo de referencia. Todas las mezclas con 8% de humedad se conformaron a 25MPa. Posteriormente se cocinaron a 950°C durante 3 horas. Los resultados obtenidos reflejan una alta factibilidad de utilización de esta biomasa para el uso estudiado. Los ladrillos cerámicos obtenidos poseen buenas características generales, con propiedades mecánicas que cumplen con los requerimientos del mercado. Además, se observó que la porosidad obtenida se relaciona con el tamaño y forma de las partículas de la biomasa utilizada, así como con la proporción agregada.