    Influence of electroplating stages on hydrogen pickup in SAE 1005 steel.
    (2018-05-10) Delpupo, Maria Noelia; Inés, Mariano Nicolás; Mansilla, Graciela Analía
    Hydrogen embrittlement is a common, dangerous, but poorly understood cause of failure in metals and alloys. In coated samples, coatings act as a barrier to hydrogen damage resulting in a decrease in the corrosion rate and consequently reducing hydrogen embrittlement. In order to obtain an effective barrier against the hydrogen income the layer must be continuous, impermeable and stable in the environment so adequate variable control must be followed. Knowledge about absorption/desorption energies of hydrogen from traps as a function of temperature help to design proper thermal treatments to eliminate it. This paper represents a survey about variables involved at each electroplating stage and hydrogen income into steel wires, analyzed through optical microscopy, scanning electron microscopy and thermal analysis.
  • Thumbnail Image
    Item
    Estudio comparativo del efecto de hidrógeno en aceros MLC 420 y SAE 1045 soldados mediante SMAW
    (2019-08-09) Inés, Mariano Nicolás; Bertucelli, Mariano Javier; Mansilla, Graciela Analía
    En este trabajo se realizaron cupones de soldaduras SMAW sobre dos grados de aceros empleando electrodos secos, posteriormente se efectuó carga electrolítica de hidrógeno (H) para simular condiciones agresivas de ingreso de este elemento sobre las probetas de tracción construidas a partir de uniones soldadas con estos consumibles. En primer lugar, el objetivo de este trabajo es comparar la respuesta mecánica de estas muestras con y sin carga electrolítica de H, y en segundo lugar, evaluar mediante la aplicación de ataque metalográfico específico, en qué sectores de la estructura del acero quedó atrapado el H.
  • Thumbnail Image
    Item
    Influencia del hidrógeno gaseoso sobre las propiedades mecánicas de un acero de alta resistencia
    (2018-10-24) Airaldi, Laureano Jesús; Inés, Mariano Nicolás; Asmus, Carolina Andrea; Delpupo, Maria Noelia; Mansilla, Graciela Analía
    La Fragilización Inducida por Hidrógeno (FIH) se ha investigado a través de los años mediante la aplicación de técnicas de carga electrolíticasde H, más rápidas y sencillas de llevar a cabo. Sin embargo, éstas no pueden replicar por completo el daño causado por el hidrógeno gaseoso en ciertas aplicaciones industriales, como ser tuberías de transporte de hidrocarburos. El fenómeno de sería el mismo si se considera una misma concentración de hidrógeno (H), independientemente del método de carga. En este trabajo se plantea la respuesta en fatiga de bajo número de ciclos de un acero resulfurado de alta resistencia, cargado con hidrógeno gaseoso (168 h a temperatura ambiente). Se evalúa la respuesta mecánica y se realizan ensayos de Calorimetría Diferencial de Barrido (DSC) para determinar temperaturas de desorción y asociarla con las eventuales trampas de hidrógeno (defectos de la red) donde pudo quedar ocluido en el acero.
  • Thumbnail Image
    Item
    Caracterización del fenómeno de corrosión sobre acero de alta resistencia
    (Universidad Tecnológica Nacional, 2019-09-14) Delpupo, Maria Noelia; Demassi, Barbara; Mansilla, Graciela Analía
    La corrosión se define como el deterioro de un material como consecuencia de un ataque electroquímico por su entorno; el cual no solo provoca el menoscabo de la superficie de los elementos y estructuras, sino que también reduce la resistencia y las propiedades mecánicas de los mismos. Un material es corroído cuando éste es destruido o deteriorado a través del tiempo debido a una reacción química o electroquímica por el medio ambiente con el cual convive. La resistencia a la corrosión depende de la composición del material y del medio ambiente en particular. El objetivo de este trabajo es evaluar la acción corrosiva sobre muestras de acero resulfurado de alta resistencia expuestas a niebla salina durante 96 h con apertura de spray mínima.
  • Thumbnail Image
    Item
    Viscosidad de polvos coladores: comparación entre valores experimentales y modelos teóricos
    (Universidad Nacional de Rosario, 2019-10-01) Santini, Leandro; Martin, Alejandro; Benavidez, Edgardo; Brandaleze, Elena
    En este trabajo se presenta el desarrollo, montaje y puesta en servicio de un equipo para realizar mediciones de viscosidad a altas temperaturas. En particular, se mide la viscosidad de tres polvos coladores comerciales formulados para el colado de aceros ULC identificados como C1, C2 y C3, por el método del cilindro rotativo en el rango de temperatura comprendido entre 1100°C y 1350°C. Los resultados se comparan con modelos teóricos de aplicación industrial, con cálculos termodinámicos empleando el software FactSage 7.2 y con la fluidez evaluada mediante el ensayo del plano inclinado.
  • Thumbnail Image
    Item
    Correlación entre viscosidad y estructuras vítreas obtenidas a partir de polvos coladores fundidos
    (Universidad Nacional de Rosario, 2019-10-01) Santini, Leandro; Desimone, Mariela; Benavidez, Edgardo; Brandaleze, Elena
    En el presente trabajo se analiza, por medio de difracción de rayos X (DRX) y espectroscopia Raman, la estructura de tres polvos coladores comerciales, obtenidos por enfriamiento rápido (templado) desde la fusión (1300°C). El análisis de la estructura es asociado a valores de viscosidad (método del cilindro rotativo) y fluidez (método del plano inclinado) obtenidos a 1300°C.
  • Thumbnail Image
    Item
    Thermal analysis techniques applied to study wear mechanisms of black refractories used in the steel continuous casting process
    (Springer, 2019-06-01) Brandaleze, Elena; Benavidez, Edgardo
    In this paper, the results are correlated with information obtained through conventional techniques such as optical microscopy (OM) and scanning electron microscopy (SEM) including EDS analysis and EBSD, that are used to characterize different structural aspects on the refractory material and of the interface with the moud flux adhered on the nozzle. The thermodynamic simulation of the corrosion also contribute with relevant information associated to the main goal of this paper. By the thermochemical simulations, the chemical reactions in the system between nozzle and mold flux are justified. All this information is useful to stablish the coorrosion mechanisms and to predict the dynamic process conditions that cause the damage in the refractory material, in order to improve the nozzle performance.
  • Thumbnail Image
    Item
    Replacement of fluorine in mould powders: influence on the crystallization kinetics
    (Springer, 2019-06-01) Benavidez, Edgardo; Santini, Leandro; Brandaleze, Elena
    In the present work mould powders were prepared using different raw materials. One powder was fluorine-containing and the others were free-F. The total fluorine content (approx. 10 wt%) was replaced by different percentages of boron, sodium and lithium oxides. Fluorspar (CaF2), borax anhydrous (Na2B4O7), and lithium carbonate (Li2CO3) were employed as source of fluorine, boron, and lithium, respectively. These powders were milling during 2 hours, then were melted at 1300°C and finally fast cooled onto a stainless steel plate. The amorphous solid layers as obtained were milling to produce glass powders which were tested by DTA at different heating rates: 5, 10, and 15°C/min. Several non-isothermal methods (Kissinger, Augis-Bennet, Ozawa, Cheng) were applied to study their kinetics of crystallization. From these models, different parameters associated to crystal growth, such as the activation energy (Ec), the frequency factor () and the nucleation rate (kc), were determined. Crystallographic phases and crystal size distribution were determined by X-ray diffraction and microscopic observation techniques.
  • Thumbnail Image
    Item
    Analysis of DTA and dilatometric data used to study the behaviour of a mould flux
    (2019-06-01) Benavidez, Edgardo; Santini, Leandro; Brandaleze, Elena
    In the present work a casting powder containing ≈ 36 wt% SiO2, ≈ 31 wt% CaO, 13 wt% Na2O, and 10 wt% CaF2, was used as starting material. A mass of 10 g of the mould powder was placed in a graphite crucible and melted at 1300°C. After 15 minutes at this temperature, the melt was poured onto a stainless steel inclined plate. By this method, solid glass layers were produced, which were sectioned into bars 10-15 mm in length to be used in dilatometric tests. Some of these bars were ground to powder to perform DTA runs. Both tests (DTA and dilatometry) were carried out at different heating rates: 5, 10 and 15 ºC/min, in air atmosphere, up to 900°C. Data of glass transition temperature (Tg), and crystallization peak temperature (Tc) were obtained from DTA and dilatometric runs. From these data, several non-isothermal methods based on Kissinger, Augis-Bennet, Ozawa, and Cheng models, were used to study the crystallization kinetics. Based on these models, the activation energy of crystallization (E), the frequency factor () and the crystallization rate constant (k) were calculated. A subsequent study was followed to determine the Avrami exponent and the crystallized fraction. The crystallographic phases were determined by XRD and the microstructure of samples, treated between 400-900 ºC, was observed by optical and electronic microscopy.
  • Thumbnail Image
    Item
    Análisis de las impurezas y el tamaño de grano en partículas de magnesia electrofundida sobre el comportamiento de refractarios MgO-C
    (Universidad Nacional de Rosario, 2019-10-01) Lagorio, Yamila; Gass, Sebastián; Benavidez, Edgardo
    El presente trabajo tiene como objetivo estudiar el comportamiento de ladrillos de MgO-C conformados con magnesia electrofundida de distintas calidades. Para esto se conformaron tres ladrillos, identificados como EF1, EF2 y EF3, los cuales fueron formulados con un contenido de MgO del 90% (de calidad electrofundida) y 8,2% de material carbonoso, difiriendo en la pureza, distribución granulométrica y tamaño de grano de las partículas de magnesia.