  • Thumbnail Image
    Item
    Carbon based DLC films : influence of the processing parameters on the structure and properties
    (2018-07-19) Delfin, Francisco Andrés; Brühl, Sonia Patricia; Forsich, Christian; Heim, Daniel
    Hydrogenated carbon-based films, such as DLC (“Diamond Like Carbon”), have interesting properties such as excellent tribological behavior, low friction coefficient, high superficial hardness and good wear resistance; they are chemically inert and highly corrosion resistant. They are deposited by means of PACVD (plasma-assisted chemical vapor deposition) with variable film thickness. The load carrying capacity grows with the thickness, so it is possible to deposit thick films on “soft” steels (e.g. low alloyed steels). When increasing coating thickness, surface defects are generated during the deposition process compromising their excellent properties. In this work, different metal substrates have been used to compare adhesion and quantify superficial defects: AISI 316L, DIN 42CrMo4 (AISI 4140) and Böhler K110 (AISI D2). The films were deposited at different temperatures, changing the silicon content and the coating thickness. The samples were placed in the furnace on different positions (standing, lying or up-side down). The films were analyzed with optical and electron microscopy, 3D topography profilometer, and they were tested under sliding wear conditions. Friction coefficient and wear volume were measured, with an average friction coefficient which resulted below 0.05. A higher amount of surface defects was obtained on lying samples compared to the ones up-side down. The quantity of defects increased with the thickness of the coating and decreased with the temperature. The geometry and the growth mechanism of the defects were analyzed.
  • Thumbnail Image
    Item
    Tribological behaviour of a multilayer CrN/DLC coating obtained using PVD-MS
    (2022-08) Delfín, Francisco Andrés.; Brühl, Sonia Patricia
    Diamond-like Carbon (DLC) coatings are used as protective layers for steel components due to their hardness, chemical inertia and interesting tribological properties. Reducing wear and friction coefficient is of great importance for industries today in order to increase energy efficiency and reduce harmful emissions to the environment. In this paper, a multilayer CrN/DLC coating is analysed. It was deposited using a commercial Plasma Enhanced Magnetron Sputtering over nitrided and not nitrided mild-alloy steel AISI 4140, produced for the first time in Argentina, at the firm Coating.Tech by Flubetech-Tantal. The base of the coating is an anchor layer made of CrN and the top layer is a chromium-dopped hydrogenated amorphous carbon (a-C:H:Cr), which provides excellent tribological properties. Wear tests were carried out in a Pin-on-Disk apparatus, using an Al2O3 ball as counterpart, with Hertzian contact stress from 1370 up to 1460 MPa. The friction coefficient was μ~0.1, which is 80% less than the untreated steel and the wear volume loss was reduced eight times. The adhesion was evaluated by means of Scratch Test, where major improvement was noticed in the samples which were nitrided as pre-treatment, increasing critical load from 25 N up to 65 N.