  • Thumbnail Image
    Item
    Boron Removal from Aqueous Solutions by Synthetic MgAlFe Mixed Oxides
    (2019-05-22) Heredia, Angélica; M. de la Fuente Garcia - Soto; Narros Sierra, Adolfo; Mendoza, Sandra; Gómez Ávila, Jenny; Cirivello, Mónica
    The boron removal capacity from an aqueous solution using MgAlFe mixed oxides from layered double hydroxides (LDH) was studied. They were synthesized by the coprecipitation method at 70 °C and were characterized as potential filter materials. The Fe3+ analyzed by X-ray photoelectron spectroscopy and UV–visible diffuse reflectance showed their tetrahedral and octahedral coordination. Scanning electron microscopy micrographs and thermogravimetric and differential scanning calorimetry analysis evidenced the presence of clusters and particles aggregates and decreased dehydroxylation temperature when the iron content increased. Mixed oxides and boron solution in a ratio of 20:1 Mg/B were put in a batch reactor at different contact times. The borate removal process was due to the memory effect of the mixed oxides and superficial adsorption by electrostatic attraction. This fact is directly related to the specific surface area, Fe content, and surface charge. The maximum boron removals were achieved with the CS25 and CS50 samples with values higher than 85%.
  • Thumbnail Image
    Item
    Compared arsenic removal from aqueous solutions by synthetic mixed oxides and modified natural zeolites
    (2019-05-09) Heredia, Angélica; Gómez Ávila, Jenny; Vinuesa, Ariel; Saux, Clara; Mendoza, Sandra; Garay, Fernando; Cirivello, Mónica
    Layered Double Hydroxides of Mg–Al–Fe and their mixed metallic oxides of high specific surface area were synthesized by the coprecipitation method. A natural zeolite from a regional quarry with high clinoptilolite content was conditioned and modified. Initially, an acid treatment was applied and subsequently Fe(III) was incorporated by the wet impregnation method. Then the prepared solid materials were characterized by XRD, N2 adsorption–desorption at 77 K, SEM, DRS UV–Vis, and MP-AES to determine their physicochemical properties. Finally, the solid materials were evaluated as adsorbents for arsenic removal in water. The tracking of As and its species concentration at trace levels was carried out by cathodic stripping Square-wave voltammetry, which has proved to be a highly selective and sensitive electrochemical method. High levels of effectiveness in terms of removal were achieved, particularly with the natural zeolites and mixed oxides of highest iron content.
  • Thumbnail Image
    Item
    Diseño de nanoarcillas aniónicas y sus óxidos mixtos para ser aplicados en tecnologías específicas de interés regional
    (2018-01-01) Mendoza, Sandra; Cirivello, Mónica
    Tanto en la provincia de Santa Fe como en la de Córdoba, se replican problemáticas ambientales comunes a otras regiones del país, como son la contaminación de recursos hídricos por la actividad agroindustrial, además de la presencia de forma natural de oxianiones, como arsénico y la producción de biomasa residual originada por procesos industriales. Para el tratamiento de dichas problemáticas, se podrían emplear materiales de características específicas, tales como los Hidróxidos Dobles Laminares. Los mismos pertenecen al grupo de las nanoarcillas, que poseen propiedades características en función de su composición. La ingesta sistemática de arsénico produce lesiones permanentes en el organismo que pueden derivar en cáncer. Estructuras estables de Oxi/Hidróxidos de MgAlFe con propiedades adsorbentes son adecuadas para la remoción de oxianiones de arsénico en aguas subterráneas y superficiales. Los fenoles residuales del uso de químicos en las actividades agropecuarias pueden degradarse por acción de catalizadores con Fe en su composición, más un oxidante verde como el H2O2. Del mismo modo, el glicerol, subproducto de la fabricación de biodiesel, biocombustible que se genera a partir de materia prima renovable, puede aumentar su valor por catálisis básica, transformándose en emulsionantes o precursores de policarbonatos. El presente proyecto tiene por objetivo definir la tecnología apropiada a través del diseño de materiales sólidos con propiedades adsorbentes y catalíticas para encontrar propuestas eco-compatibles a los problemas planteados. Estos materiales funcionalizados y aplicados en los procesos expuestos serán sintetizados en la Facultad Regional Córdoba, y serán caracterizados por medio de los equipos de detección de composición, morfología y topografía de la Facultad Regional de Reconquista.