UTN- FRC -Producción Académica de Investigación y Desarrollo
Permanent URI for this communityhttp://48.217.138.120/handle/20.500.12272/1932
Browse
3 results
Search Results
Item Novel mesoporpous carbon modified with zirconia for hydrogen adsorption.(Univesidsad Tecnológica Nacional., 2021) Venosta, Lisandro; Juárez , Juliana María; Anunziata , Oscar Alfredo; Gómez Costa, Marcos Bruno; Anunziata , Oscar Alfredo; Juárez , Juliana MaríaNanostructured carbon material (CMK-3) modified with zirconium oxide was synthesized by a new direct synthesis technique. Zirconium oxide dispersed in carbon materials (Zr-CMK-3) were characterized by X-ray diffraction, textural properties, UV-Vis-DRS, XPS, and transmission electron microscopy analysis. The goal of this new synthesis method is to avoid the use of inorganic siliceous template (SBA-15), which leads to a shorter and cheaper way to obtain mesoporous carbon, and at the same time incorporate into the framework Zirconium atoms. Zr-CMK-3 material significantly improved H2 storage behaviour (4.6% by weight at 77 K and 10 bar) compared to CMK-3 support. The synthesized material is promising in the absorption of hydrogen by weak bonding forces (physisorption). The activity of the samples to the adsorption of hydrogen molecules is attributed to the improved dispersion of the zirconium oxide, as well as the appropriate use of support, which can probably disperse the zirconium on its large surface area, allowing a great dispersion of the zirconium. The Zr+4 cation is an active species to absorb and store hydrogen through a physisorption process and the carbon plays an important role in the dispersion and size of metal particles. A hydrogen storage mechanism on the active surface of the ZrO2 clusters was proposed. First layer of hydrogen molecules can react with the metal cation through a dihydrogen complex (Kubas interaction). The second layer of hydrogen molecules adsorbed around the metal oxide clusters is due to dipole-like interactions, this is because the metal particle induces dipole forces on the hydrogen molecule. The other layers could also interact by dipole forces; however, the interaction force decreases as the distance to the surface increases. The upper layers could interact with the metal cation by dipole-induced bonding; however, the interaction force decreases as the distance to the surface increases.Item Preparation and characterization of activated CMK-3 modified with vanadium applied in hydrogen storage.(Univesidsad Tecnológica Nacional, 2024) Juárez , Juliana María; Gómez Costa, Marcos Bruno; Cussa , jorgelina; Anunziata , Oscar Alfredo; Anunziata , Oscar Alfredo; Cussa , jorgelinaThe aim of this work is to synthesize a nanostructured Carbon CMK-3 modified with V in order to increase its capacity in hydrogen storage. The approach that we have followed includes synthesis of nanostructures with the experimental study of its adsorption capacity and storage properties. Ordered nanoporous carbon CMK-3 was synthesized via a two-step impregnation of the SBA-15 mesopores with a solution of sucrose using an incipient wetness method. The sucrose–silica composite was heated at 1173 K for 4 h under nitrogen flow. The silica template was dissolved with 5 wt% hydrofluoric acid in order to remove the silica. The template-free carbon product thus obtained was filtered, washed with deionized water and ethanol, and dried. [1] V-CMK-3 was prepared by wetness impregnation using VCl3 as source of Vanadium in order to increase the amount of hydrogen adsorbed. The sample of V-CMK-3 was treated under H2 flow two times at 1173 K. Porous carbon CMK-3 and the sample modified with V were characterized by XRD, FTIR, XPS, BET, TEM and SEM. These studies indicate that it was possible to obtain a CMK-3 replica successfully from SBA-15, using sucrose as a carbon precursor. [2] The surface areas are 1320 m2/g and 1050 m2/g for CMK-3 and V-CMK-3, respectively. While the nanomaterial area is significantly smaller with the incorporation of the metal, CMK-3`s characteristic structure is maintained after the metal is within the host, in agreement with the XRD studies. Measurements of hydrogen adsorption at cryogenic temperatures and low pressures were performed. The nanoparticles of V incorporated onto the nanostructured carbon CMK-3 showed higher hydrogen uptake at low and high pressures than CMK-3. (3.4 wt% and 2.2 wt% respectively of H2 sorption at 10 bar and 77 K).Item Synthesis and characteristics of CMK-3 modified with magnetite nanoparticles for application in hydrogen storage.(Univesidsad Tecnológica Nacional, 2020) Venosta, Lisandro; Juárez , Juliana María; Anunziata , Oscar Alfredo; Bercoff, Paula; Gómez Costa , Marcos Bruno; Anunziata , Oscar Alfredo; Juárez , Juliana María: In this work, we report the synthesis and characterization of iron oxide nanoparticles supported in nanostructured carbon (CMK-3). This material is promising in the application of hydrogen adsorption for energy storage. The material with iron oxide nano particles (Fe-CMK-3) was successfully synthesized and characterized by X-ray diffraction, textural properties analysis, transmission and scanning electron microsco py, X-ray photoelectron spectroscopy, and magnetiza tion studies. A large amount of the iron incorporated as iron oxide nanoparticles was in the magnetite phase. The incorporation of magnetite on the CMK-3 carbon surface significantly improved the storage capacity of hydrogen (4.45 wt% at 77 K and 10 bar) compared with the CMK-3 framework alone (2.20 wt% at 77 K and 10 bar). The synthesized material is promising for hy drogen adsorption by weak bond forces (physisorption). A hydrogen adsorption mechanism was proposed in which the nanoparticles of magnetite have an important role.