    Desgaste por fretting en un recubrimiento de nitruro de titanio depositado sobre de AISI 316L nitrurado
    (2021-10-05) Vaca, Laura Silvia; Quintana, Juan Pablo; Maskavizan, Ana Justina; Cabana Aranda, Federico Ezequiel; Márquez, Adriana Beatriz; Brühl, Sonia Patricia
    Los aceros inoxidables austeníticos son requeridos para su uso en ambientes agresivos debido a su excelente resistencia a la corrosión, pero a fin de ampliar el rango de aplicación es necesario tratarlos superficialmente para elevar su dureza y mejorar su resistencia al desgaste. Si entre dos componentes de un sistema que están en contacto se origina un movimiento oscilatorio de pequeña amplitud es posible que se produzca desgaste por fretting, lo que podría causar una falla que afecte su funcionamiento. El objetivo de este trabajo es evaluar el comportamiento al desgaste por fretting de recubrimientos de TiN depositados por arco catódico sobre acero inoxidable AISI 316L nitrurado por plasma. Se compararon los volúmenes desgastados de un recubrimiento comercial de TiN y recubrimientos bicapa de Ti-TiN combinando éste con implantación iónica. Como referencia fueron evaluadas muestras solamente nitruradas y el acero sin tratar. El ensayo se realizó durante 15, 30 y 60 minutos con una carga de 5 N y se utilizó como contraparte una bolilla de alúmina de 6 mm. Para los ensayos de mayor tiempo los volúmenes desgastados de los recubrimientos no mostraron diferencias y resultaron al menos 40% menores que los de las muestras nitruradas y 70% menores que los del acero sin tratar. Sin embargo, para los ensayos de 15 minutos, los recubrimientos bicapa de Ti-TiN combinados con implantación iónica presentaron el mejor comportamiento al desgaste por fretting, al obtener un menor volumen desgastado y no dejar expuesto al sustrato.
  • Thumbnail Image
    Item
    DLC multilayers to improve fretting and corrosion resistance over nitrided martensitic stainless steel
    (2018-09-20) Brühl, Sonia Patricia; Dalibón Bähler, Eugenia Laura; Trava-Airoldi, Vladimir Jesús
    In this work, the fretting wear and corrosion behavior of DLC multilayers coatings were studied and compared to the monolayer coating.
  • Thumbnail Image
    Item
    Soft and thick DLC deposited on AISI 316L stainless steel with nitriding as pre-treatment tested in severe wear conditions
    (2020) Dalibón Bähler, Eugenia Laura; Moreira, Ramiro Damián; Heim, Daniel; Forsich, Christian; Brühl, Sonia Patricia
    Thick and soft DLC coatings were deposited over stainless steel to improve their surface properties, protecting them from wear in different conditions. When a protective film is thick, it can be considered as self­sustaining in terms of load­carrying capacity during wear situations even if the substrate is soft or hard. Thin and hard DLC coatings are well known for having high hardness and low friction coefficient; however they have adhesion problems when deposited on soft steels and many of their wear properties also depend on adhesion. For this reason, a previous plasma nitriding process may be convenient. In this work, the fretting and erosion wear behaviour of DLC soft coatings deposited on nitrided and non­nitrided austenitic stainless steel was evaluated using high loads and long tests both simulating severe conditions wear. The aim is to analyse under which conditions the film thickness is not enough to withstand wear damage when deposited onto soft steels. The results showed that in the fretting tests, the duplex sample presented better resistance than the only coated sample in all tested conditions, except for the minimum load, 12 N. In slurry erosion tests, the mass loss was similar in both samples until nine hours, when the influence of the nitrided layer became noticeable as a hard layer since the coating partially removed.