    Estudio de la erosión y la corrosión en AISI 420 recubierto con DLC soft, con y sin nitruración previa
    (2017-08-17) Dalibón Bähler, Eugenia Laura; Moreira, Ramiro Damián; Silva, Kevin Daniel
    Los aceros inoxidables martensíticos tienen múltiples aplicaciones donde se requiere buena resistencia al desgaste y a la corrosión. Para mejorar sus propiedades superficiales se pueden utilizar recubrimientos tipo DLC (Diamond Like Carbón). Estos presentan problemas de adhesión cuando son depositados sobre sustratos metálicos; por esta razón, un tratamiento previo de nitruración podría resultar conveniente. En este trabajo se analizo el comportamiento a la erosión y corrosión de muestras de AISI 420 recubiertas con DLC Soft por PACVD (Plasma Assisted ChemicalVapour Deposition) templadas y revenidas (muestras recubiertas) y nitruradas (muestras dúplex). También se determino como afecta un tratamiento de nitrurado previo en los resultados. La micro estructura de la capa nitrurada y de los recubrimientos se analizo mediante microscopia óptica y SEM. Los recubrimientos se caracterizaron por Espectroscopia Raman y EDS. Se midio dureza superficial de las muestras. La adhesión fue evaluada con Scratch Test e Indentacion Rockwell C. Se realizaron ensayos de corrosión potenciostáticos y de erosión. Los resultados de este ultimo se compararon con los obtenidos para muestras templadas y revenidas, y nitruradas. El espesor del recubrimiento fue de 25 um y la capa nitrurada de 17 um. La dureza del recubrimiento fue de 828 HV y la capa nitrurada de 1040 HV. En los ensayos de Scratch Test y de indentación, la nitruración previa mejoro la adhesión. Se observo una mejora en el comportamiento a la corrosión en las muestras dúplex. Esto esta vinculado a la cantidad y tipo de defectos que presentan los recubrimientos. En cuanto a los ensayos de erosión, las muestras solo recubiertas y dúplex presentaron unos comportamientos similares al de las muestras solas nitruradas debido a que parte del recubrimiento se desprendió durante el ensayo.
  • Thumbnail Image
    Item
    Characterization of DLC coatings over nitrided stainless steel with and without nitriding pre-treatment using annealing cycles
    (2019-04-02) Dalibón Bähler, Eugenia Laura; Czerwiec, Thierry; Trava-Airoldi, Vladimir Jesús; Ghafoor, Naureen; Rogström, Lina; Odén, Magnus; Brühl, Sonia Patricia
    Amorphous hydrogenated diamond-like carbon (DLC) coatings were deposited using plasma assisted chemical vapour deposition (PACVD) on precipitation hardening (PH) stainless steel. Plasma nitriding has been used as pre-treatment to enhance adhesion and mechanical properties. Chemical and mechanical properties of DLC coatings are dependent on the hydrogen content and so on the relation between sp3 /sp2 bondings. The bondings and the structure of the DLC film change with temperature. In this work, a study of the thermal degradation and the evolution of the mechanical properties of DLC coatings over PH stainless steel have been carried out, including the effect of an additional nitrided layer. Nitrided and non-nitrided steel samples were subjected to the same coated in the same conditions, and they were submitted to the same thermal cycles, heating from room temperature to 600 C in several steps. After each cycle, Raman spectra and surface topography measurements were performed ◦ and analyzed. Nanohardness measurements and tribological tests, using a pin-on-disc machine, were carried out to analyze variations in the friction coefficient and the wear resistance. The duplex sample, with nitriding as pre-treatment showed a better thermal stability. For duplex sample, the coating properties, such as adhesion, and friction coefficient were sustained after annealing at higher temperatures; whereas it was not the case for only coated sample.
  • Thumbnail Image
    Item
    Comparación del comportamiento al desgaste de un acero AISI 1045 nitrurado y seguido de un temple por inducción
    (2016-10) Schierloh, Gonzalo José; Regis, Matías Sebastián; Charadía, Raúl; Dalibón Bähler, Eugenia Laura; Brühl, Sonia Patricia
    Se estudió el comportamiento al desgaste del acero AISI1045 con un tratamiento de nitruración iónica y posterior temple por inducción. Se midió dureza en superficie y perfil en profundidad. Se analizó la microestructura y evaluó el comportamiento al desgaste. Como resultado de la nitruración se obtuvo una zona formada por una capa de compuestos seguida por una zona de difusión de nitrógeno. La dureza superficial del acero templado y revenido aumentó en un 50% y, con el temple por inducción posterior, resultó aún superior con incremento en la dureza del núcleo. El comportamiento al desgaste resultó mejor que la del acero sólo nitrurado, debido al incremento de la capacidad de soporte de carga del sistema.