Facultad Regional San Nicolas
Permanent URI for this communityhttp://48.217.138.120/handle/20.500.12272/110
Browse
7 results
Search Results
Item Incidence of heat treatment on the corrosive behavior of AISI 316L austenitic stainless steel(2023-06-30) Inés, Mariano Nicolás; Mansilla, Graciela AnalíaHeat treatments of AISI 316L samples were conducted at 900°C with slow cooling in air to induce varied precipitation of chromiumrich carbide particles at grain boundaries, resulting in a microstructure susceptible to intergranular corrosion. The corrosion behavior of the material in this state was investigated in a salt spray chamber containing 5% NaCl. The temperature inside the chamber was set at 35°C, while the saturated air temperature was recorded at 47°C. Samples were periodically extracted for observation and analysis using a stereoscopic magnifying glass, optical microscope, and scanning electron microscope. The results revealed the detrimental effect of chloride ions on the corrosion behavior of these stainless steels. Metallographic examination of corroded specimens after the salt spray test confirmed that the passive layer's breakdown was responsible for the intergranular corrosion occurring along preferential paths of chromium carbides.Item Sensitización microestructural en acero inoxidable austenítico AISI 316L(2022-11-08) Inés, Mariano Nicolás; Mansilla, Graciela AnalíaA pesar de los numerosos intentos por desarrollar aceros inoxidables austeníticos con adiciones intencionales de elementos de aleación para mitigar las reacciones corrosivas que pueden originarse durante el servicio en ambientes agresivos, estas condiciones operativas pueden causar daños microestructurales en bordes de grano y, en consecuencia, una disminución de la ductilidad y pérdida de resistencia mecánica. Además, el ataque se ve agravado por las partículas de carburo desarrolladas durante ensayos de sensitización, ya que la formación de éstos conduce a una disminución del contenido de cromo en las cercanías a los límites de grano, dejando a la aleación susceptible a corrosión intergranular cuando se los expone a atmósferas inadecuadas. En este trabajo, se somete a muestras de acero inoxidable austenítico AISI 316L a tratamiento térmico de solubilización a 1100 °C durante 1 hora, y enfriamiento en agua (set 1) y en aire (set 2). Posteriormente, se realiza sobre éstas tratamiento de sensitización isotérmico durante 6 horas, con enfriamiento en horno. Del análisis microestrutural llevado a cabo es posible establecer una relación directa entre la cinética de enfriamiento, los carburos desarrollados y el grado de sensitización evidenciado en las muestras. Se determinaron ataques intensos en bordes de grano austenítico, lo que estaría dejando en evidencia, en principio, la eficacia del tratamiento de sensibilización aplicado. En una etapa posterior, se realizarán ensayos de corrosión acelerada sobre las muestras sensibilizadas microestructuralmente con el objetivo de estudiar su comportamiento en corrosión y analizar el posible daño generado.Item Efecto de la velocidad de deformación en ensayos de tracción de acero inoxidable AISI 316L(Ing. Marta Caligaris - Dra. Nancy Quaranta - Ing. Fernando Palmieri, 2021-09-15) Inés, Mariano Nicolás; Mansilla, Graciela AnalíaEn este estudio se presentan los resultados obtenidos de la investigación llevada a cabo para determinar la interacción existente entre los carburos de cromo y el hidrógeno en muestras de acero inoxidable AISI 316L, y su posible incidencia en el comportamiento mecánico considerando distintas velocidades de deformación en ensayos de tracción. Para lograr una microestructura susceptible, con una distribución homogénea de carburos, se desarrollaron tratamientos térmicos con enfriamiento en aire, y luego sobre un grupo de estas muestras se llevaron a cabo cargas electrolíticas de hidrógeno, empleando una solución electrolítica de H2SO4 1N, con 0,25 g/L de NaAsO2 como agente promotor de hidrógeno, un ánodo de grafito y una densidad de corriente constante de 35 mA/cm2 durante 3,5h. Para finalizar, se realizaron sobre el total de las muestras ensayos de tracción, considerando dos velocidades de desplazamiento del cabezal, de 0,5 mm/min y 5 mm/min, respectivamente. Las superficies de fractura resultantes, independientemente de la velocidad de desplazamiento del cabezal, exhibieron un comportamiento mixto dúctil - frágil en muestras cargadas con hidrógeno junto con grietas asociadas con los carburos de cromo, en comparación con la morfología netamente dúctil (con dimples bien desarrollados) obtenida en aquellas sin carga. Las curvas tensión-deformación, para ambas velocidades demuestran que existen variaciones entre la tensión de rotura y la máxima elongación. Para evidenciar las interacciones del hidrógeno con las microestructuras obtenidas, se aplicó una técnica metalográfica selectiva, logrando identificar a los bordes de grano y las interfaces de carburos / matriz como las principales trampas de hidrógeno. Estos resultados permitieron determinar que los carburos desarrollados causan atrapamiento perjudicial de hidrógeno y son responsables del comportamiento mecánico medido en el acero inoxidable AISI 316L.Item Salt spray test on AISI 316L stainless steel(2020-01-10) Inés, Mariano Nicolás; Mansilla, Graciela AnalíaDamage produced by rigorous working conditions can affect materials, especially when they are exposed to high temperatures, corrosive atmospheres and mechanical stresses. Austenitic stainless steels have variable chromium contents but greater than 16%, which allows the surface formation of a passivating thin layer of chromium oxide (Cr2O3) that protects the steel against corrosion during prolonged exposure to aggressive environments. From a metallurgical point of view, these steels meet the requirements to operate under prolonged exposures to high temperature and aggressive environments (depending on the steel grade), however attention must be paid to the precipitation of different carbides, such as M23C6 and M6C, and especially sigma () phase formation, since its precipitation produced chromium depleting zones which are very harmful in many applications, because it makes the material brittle and allows high corrosion penetration. Another consequence is sensitize hydrogen capture originated during corrosion. The aim of this work is to evaluate the corrosive behavior of an austenitic stainless steel (AISI 316L) that was first exposed to several heat treatments conditions and then was subjected to a spray saline solution of 5% NaCl, inside the chamber the temperature was set in 35ºC while the saturated air temperature was 47ºC. Characterization techniques such as optical and scanning electron microscopy were applied. Results allowed to establish the incidence on the corrosion rate of formed chromium carbides, that sensitize steel to the attack of chloride ions responsible of pitting corrosion by breaking of the passive layer thus helping a rapid corrosion rate.Item Corrosión acelerada de acero inoxidable austenítico AISI 316L previamente sensibilizado(Ing. Andrés Giuliani - Esp. Ing. Rodrigo Leurino - Ing. Victor H. J. Marelli - Esp. Ing. Sebastián Russillo, 2023-09-23) Inés, Mariano Nicolás; Mansilla, Graciela AnalíaEl estudio de la corrosión que sufren muchas estructuras y elementos construidos a base de acero inoxidable cuando en servicio se los somete a condiciones de trabajo no ideales (atmósferas agresivas) es un tema de creciente interés en la literatura. Largos tiempos de exposición a elevadas temperaturas (450ºC a 850ºC) pueden generar que la resistencia del límite de grano pueda verse afectada por la precipitación de carburos intergranulares (principalmente, M23C6 y M6C), y en especial la formación de fase sigma, responsables del daño intergranular en este tipo de acero. Entonces, especial atención debe prestarse ya que estos carburos son sensibles a la captura del hidrógeno originado como consecuencia de reacciones corrosivas. En este trabajo se evalúa el comportamiento microestructural de un acero inoxidable AISI 316L sometido a ensayo de corrosión acelerada, considerando distintos tiempos de exposición a una atmósfera salina, esto es, 8h, 50h y 96h. Las muestras fueron previamente solubilizadas a 1100°C durante 1h, y luego enfriadas en agua y otras en aire. Posteriormente, éstas fueron sensibilizadas isotérmicamente a 650°C durante 6h, con enfriamiento lento en horno. Del análisis microestrutural realizado en las muestras sensibilizadas, se determinaron ataques intensos en bordes de grano austenítico, posiblemente atribuidos a la precipitación de partículas submicroscópicas de carburos de cromo y fases intermetálicas. Ahora bien, como resultado de los ensayos de corrosión, se destaca que, la mayor velocidad de degradación y pérdida de masa por unidad de tiempo (en un ambiente altamente clorado) la evidenció la muestra con enfriamiento en aire, en comparación con su par enfriada en agua. En una etapa posterior, se analizará el posible ingreso de hidrógeno y su impacto como consecuencia de los ensayos de corrosión en niebla salina llevados a cabo en AISI 316L bajo las condiciones experimentales definidas en este trabajo.Item Incidencia del hidrógeno atrapado sobre el comportamiento mecánico de acero inoxidable AISI 316L tratado térmicamente(2021-06-25) Inés, Mariano Nicolás; Mansilla, Graciela AnalíaEn este estudio se presentan los resultados de la investigación para evaluar las posibles interacciones entre un ambiente hidrogenado altamente agresivo y las tensiones uniaxiales aplicadas mediante ensayos mecánicos de tracción en acero inoxidable AISI 316L. Se desarrollaron tratamientos térmicos en un acero inoxidable AISI 316L (enfriado en aire) y luego sobre un conjunto de estas probetas se llevaron a cabo cargas electrolíticas de hidrógeno, considerando una solución electrolítica de H2SO4 1N, con 0,25 g/L de NaAsO2 como agente promotor de hidrógeno, empleando un ánodo de grafito y una densidad de corriente constante de 35 mA/cm2 durante 3,5h. Para finalizar, se realizaron sobre el total de las muestras ensayos de tracción considerando desplazamiento del cabezal de 0,5 mm/min. Se concluye que el acero inoxidable AISI 316L, con tratamiento térmico y cargado electrolíticamente con hidrógeno, presentó modo de fractura mixta (dúctil-frágil). Las grietas de naturaleza transgranular e intergranular encontradas están en consonancia con la distribución y morfología de los dimples desarrollados durante los ensayos mecánicos.Item Tratamientos térmicos y corrosión en niebla salina en acero inoxidable AISI 316L(Universidad Tecnológica Nacional, 2020-10-06) Inés, Mariano Nicolás; Mansilla, Graciela AnalíaEn este trabajo se evalúa el comportamiento microestructural de un acero inoxidable AISI 316L, tratado térmicamente y sometido a ensayos de corrosión acelerada, durante 96 horas, en cámara de niebla salina según normas ASTM B117 e ISO 9227. Se destaca que este material tratado térmicamente y enfriado en aire fue el que presentó mayor grado de corrosión, hallándose relación directa entre las partículas de carburo de cromo y la presencia de grietas asociadas con los productos de la corrosión.