Desarrollo, Producción e Innovación en la Investigación científica
Permanent URI for this communityhttp://48.217.138.120/handle/20.500.12272/2392
Browse
3 results
Search Results
Item HaP/SBA-3 Nanostructured Composite to Remove Fluoride Effectively from Contaminated Water.(Univesidsad Tecnológica Nacional, 2021) Cussa, Jorgelina; López , Claudia; Anunziata, Oscar Alfredo; Anunziata, Oscar AlfredoHighly ordered pore mesoporous silica composites, like SBA-3 and hydroxyapatite (HaP) nanocrystals, characterized by X-ray diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM) and textural properties, were successfully applied to remove fluoride from contaminated water. The proposed procedure to prepare HaP/SBA-3 wassuccessful, which acts as supports to anchor the HaP crystals, in nanometer-scale (<2nm), with higher fluoride retention from contaminated water. The free OH- groups of HaP nanocrystals, within the host, facilitated the high-performance fluoride trapping. The fluoride retention activity was much higher than that of pure HaP and the composites HaP/SBA-15 and HaP/MCM-41.Item Synthesis, characterization and catalytic performance of bimetallic Ir-Pt catalysts for tetralin hydrogenation(2014) Vallés, Verónica; Ledesma, Brenda; Rivoira, Lorena Paola; Cussa, Jorgelina; Martínez, María Laura; Anunziata, Oscar Alfredo; Beltramone, Andrea RaquelBimetallic Pt–Pd catalysts have received considerable attention, because they show high activity in a variety of catalytic applications (1) and stability compared with monometallic Pt or Pd catalysts. For instance, the bimetallic Pt–Pd catalysts have been shown to have higher resistance toward poisonscompared to Pt catalysts (2-4). For supported bimetallic clusters, the surface and bulk composition strongly depend on a series of parameters, for example, preparation procedures, metal–metal and metal–support interactions. The final goal is to find the optimal proportion of each metal in order to be more active in these processes.In this case a series of Ir and Pt modified SBA-15 were prepared by the consecutive wet impregnation method, with different content of each metal. The final catalysts were characterized by XRD, TEM and H2 chemisorption to study the effect of content of metal on the dispersion of iridium/platinum. The catalysts synthesized with similar percentage of both metal showed the best activity measured in tetralin hydrogenation. Platinum (Pt) and Iridium (Ir) nanoparticles were incorporated into SBA-15 support [1-4] by the wet co-impregnation method. The metal precursors were Iridium acetylacetonate and cloroplatinic acid. The samples were calcined at 500°C and previous to the catalytic test the samples were reduced by heating at 2°C/min to 450°C in a H2 stream for 5 h. Hereinafter this catalyst will be referred as Ir-Pt- SBA-15 (x), with x= 1-3. The catalytic activity was measured in a 4563Parr reactor, at 250°C, 15 atm of pressure of hydrogen and 360 rpm for tetralin hydrogenation (feed consisted in 50 mL of 5% v/v of tetralin (98.5% FLUKA) in Dodecane). The Pt-Ir-SBA-15 catalyst with 1 %wt. of each metals had the highest activity measured in tetralin hydrogenation at mild conditions. The good activity was correlated with higher Ir/Pt dispersion on SBA-15 mesostructured material used as support, as we seen by TEM and H2 Chemisorption, with higher active metal sites exposed to reactant. The Ir-Pt-SBA-15 activity is sufficiently high to envisage use in the final stages of a refinery process producing diesel fuel of high Cetane Number by hydrodearomatization.Item Tetralin hydrogenation and ring opening of decalin over Ir-Pt-SBA-15(2014) Vallés, Verónica; Rivoira, Lorena Paola; Ledesma, Brenda; Cussa, Jorgelina; Anunziata, Oscar Alfredo; Beltramone, Andrea RaquelA series of Ir and Pt modified SBA-15 were prepared by the consecutive wet impregnation method, with different content of each metal. The final catalysts were characterized by XRD, TEM and H2 chemisorption to study the effect of content of metal on the dispersion of iridium/platinum. The catalysts synthesized with similar percentage of both metals showed the best activity measured in tetralin hydrogenation and ring opening of decalin at mild conditions.