    Synthesis of ordered mesoporous SBA-3 materials using silica gel as silica source
    (2014) Martínez, María Laura; Ponte, María Virginia; Anunziata, Oscar Alfredo; Beltramone, Andrea Raquel
    Nanostructured materials have exceptional and highly attractive properties, including catalyst, adsor- bent, separation media and chemo sensor. Technical advances in these fields require the development of ordered porous materials with controllable structures, systematic tailoring pore architecture and the synthesis of mesoporous materials using a more economical silica source. Ordered mesoporous silica SBA-3 material has been synthesized successfully using cetyltrimethylamonium bromide (CTAB) as a structure-directing agent, NaOH and inexpensive silica gel as a silica source without additives. We studied the influence of NaOH concentration on the structure and morphology of mesoporous silica SBA-3. This variation was defined as modulus L ¼[NaOH/SiO2] ratio. The structural order of the samples was found to be greatly affected by L variations. The results suggest that, by controlling the L value (0.70–1), SBA-3 is obtained with appropriate physicochemical characteristics.
  • Thumbnail Image
    Item
    New synthesis of SBA-3 mesoporous material using silica gel as silica source
    (2014) Martínez, María Laura; Ponte, María Virginia; Anunziata, Oscar Alfredo; Beltramone, Andrea Raquel
    One of the main areas of interest in materials chemistry is the synthesis of mesoporous molecular sieves with highly controllable morphologies for the purpose of providing catalytic, separation, and adsorption applications to industry. The main drawback is that the expensive source of silicon as alkoxide (Si(OEt)4 or Si(OMe)4) prevents any application where large amounts of materials are required [1–2]. Ordered mesoporous silica material has been synthesized successfully by using cetyltrimethylamonium bromide (CTAB) as a structure-directing agent and inexpensive silica gel dissolved in a solution of sodium hydroxide, as the silica source without any additives. The synthesis is performed at room temperature in the presence of hydrochloric acid. The analysis of X ray diffraction shows that the resultant mesoporous materials possess an hexagonal mesostructure. We studied the effect of the initial NaOH concentration and the synthesis time on the structure and morphology of mesoporous silica SBA-3. The crystal size and structural order of the samples were found to be greatly affected by NaOH variations. The results suggest that, if the NaOH concentration increases reaching values higher than 1 M, the SBA-3 is not generated, since there is no precipitation or formation of silica gel in the reaction, appearing the corresponding disordered or amorphous silica. Whereas, when time increase from 45 min to 120 min, with molar concentration of NaOH of 0.75, the material obtained show a hexagonal mesostruture observed in the XRD pattern.